Titanium Grade23(UNS R56401) is an alpha-beta mix subject to Grade 5. It is the higher flawlessness perception of assessment 5 by decreasing the level of interstitial parts (O, N, C) and improved weight use detaching. The properties of good quality, lightweight, wonderful isolating square and radiant making it particularly fitting for thick-divider basically reliant on parts, for example, a genuine dental and restorative application.It is a basic provider and producer of evaluation Ti-6Al-4V-ELI material. It on an especially essential level stock Titanium Grade23 tubing, Titanium Grade23 sheet and Titanium Grade 23 round bar in different size and wraps up.
Titanium is lightweight, solid, isolating verified and endless in nature. Titanium and its blends have unyielding attributes from 30,000 psi to 200,000 psi (210-1380 MPa), which are inside and out that truly matters dubious from those characteristics found in an enormous section of amalgam steels.
The thickness of titanium is just 56 percent that of steel, and its usage requirement separates well and that of platinum. Of the noteworthy number of sections on the planet's outside layer, titanium is the ninth all around rich.
Titanium has a high dissolving explanation behind 3135°F (1725°C). This dissolving point is around 400°F (220°C) over the consolidating inspiration driving steel and by and large 2000°F (1100°C) over that of aluminum.
|Specifications||:||ASTM B348/ ASTM SB348|
|Dimensions||:||EN, DIN, JIS, ASTM, BS, ASME, AISI|
||:||5 mm To 500 mm|
|Diameter||:||0.1 mm to 100 mm|
|Length||:||100 mm To 3000 mm Long & Above|
|Finish||:||Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish|
|Tolerance||:||H8, H9, H10, H11, H12, H13K9, K10, K11, K12 or as per clients’ requirements|
|Form||:||Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc.|
|Ti||C Max||Fe Max||H Max||N Max||O Max||V||Al|
3.7035 / 3.7165 / 3.7235
R50400 / R56400 / R52400
|Melting range||Max 1650 °C|
|Tensile strength, min||860 MPa|
|Yield strength, 0.2% offset, min, Mpa||790 MPa|
|Elongation at Break, %||10|
|Hardness, Rockwell B||30-35|
|Badhi||And Many More|