Okay need to buy SS sheets and plates for your mechanical applications? Expecting amazingly, by then Stainless Steel 316H Sheets and Plates is the right choice for you. There are diverse creator and supplier in the market regardless you can grab this SS thing at the smart expense at Padmavati Steel & Engg.Co. This component of SS offers distinctive exceptional features, for instance, use restriction, high stacking cutoff, warm quality, precise estimations, solid updates, and some more. These SS plates are sold in mass structure and are made by satisfy undeniable endeavors governs and are made to meet the specific need of the customers.
It comes in ASTM A240 and ASME SA240 and has estimations, for instance, DIN, BS, JIS, GB, EN, AISI, etc. The Stainless Steel 316H Sheets and Plates are open in various structures, for instance, plain sheet, Designer sheet, seem sheet, checkered plate, and others. It is open in tantamount examinations, for instance, 316H UNS (S31609) and DIN (1.4401). It is open in following length 2000mm, 2440mm, 3000mm, 5800mm, 6000 mm, etc.
Stainless Steel 316H Sheets and Plates is available in thickness go 0.3mm to 6mm and hardness is offered by ASME An and NACE MR 175. It is connected by surface coatings, for instance, confirmed, painted, hot moved plate and cold moved sheets, SATIN (met with plastic checked) and others. The extent of this plate and sheet is ¼ to 4. The Stainless Steel 316H Sheets and Plates is tried well to check the thing quality and are pulverized well in order to keep up a key segment from any kind of outside mischief.
Standard : ASTM / ASME A240 / SA240
Size : 1000 mm x 2000 mm, 1220 mm x 2440 mm, 1500 mm x 3000 mm, 2000 mm x 2000 mm, 2000 mm x 4000 mm
Thickness :0.01 mm to 250 mmThk
Form : Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Strip, Flats, Blank (Circle), Ring (Flange)
Finish : Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated)
Hardness : Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc.
STANDARD | WERKSTOFF NR. | UNS |
SS 316H | 1.4401 | S31609 |
Element | SS 316H |
C | 0.10 max |
Mn | 2.0 max |
Si | 0.75 max |
P | 0.045 max |
S | 0.030 max |
Cr | 16 – 18 |
Ni | 10 – 14 |
Mo | 2 – 3 |
Fe | 68.89 min |
Element | SS 316H |
Density | 8.0 g/cm3 |
Melting Point | 1400 °C (2550 °F) |
Tensile Strength | Psi – 75000 , MPa – 515 |
Yield Strength (0.2%Offset) | Psi – 30000 , MPa – 205 |
Elongation | 35 % |